Type

  • Varetype:
    VISCOTAQ Viscowrap-HT
  • Varenummer:
    85000033
  • Egenskaper:
    VISCOTAQ is a unique viscous-elastic non crystalline a-polar polyolefin for the protection of shaped and non-shaped substrates. VISCOTAQ offers the pipeline industry an unrivaled technology when it comes to corrosion prevention. Unlike other coatings VISCOTAQ always has a permanent and intimate contact with the surface of a substrate. The viscosity and elasticity modulus of the material are designed in such a way that the viscosity modulus provides permanent wetting characteristics hence forcing the material to flow into the pores and anomalies of the substrates whereas the elasticity modules provides the strength and elasticity of a solid.
  • Leveringsenhet:
    Roll 20cm x 10mtr

Teknisk informasjon

  • Funksjon:
    - Corrosion preventing - Sealing
  • Produkt informasjon:
    VISCOWRAP-HT is a non crystalline a-polar viscous elastic solid polyolefin coating in roll form used for the protection of under- and aboveground substrates against corrosion. VISCOWRAP is a 2-layer system that consists of a corrosion protective inner wrap (VISCOWRAP) and mechanical protective outer wrap that can be a PE, PVC or PU composite outer wrap.
  • Applikasjon:

    - Temperature range -35° C/-31° F upto +100° C/+212° F

    - Continuous operating temperature up to 80° C/+176° F

    - Application temperature > +5° C/+41° F

    - Recommended surface preparation SA 2-1/2 or SSPC/SP-10

    - Surface preparation minimum SSPC/SP-2

    - Application minimum +3° C/+37,4° F above dew point

Annen informasjon

  • Fordeler:

    - Melting point +152,8° C/+307,04° F

    - Glass transition temperature -35° C/-31° F

    - CD value 0-3 mm (ASTM G8) at +23° C/+73,4° F

    - Self healing in case of small damages

    - Impervious to moisture and gases

    - Adhesion to the substrate without primer

    - Remaining flexibility over decades

    - Easy in use; can be cut and paste

    - Permanent wetting characteristics

    - Eliminates Microbiological Induced Corrosion (MIC)

    - No curing time

    - Extreme high chemical resistance

    - No sensitivity to salts and osmosis

    - Cohesive fracture

    -100% inert formulation: no reactive groups and no deterioration in the course of time